制作中空玻璃設(shè)備的原片玻璃可所以無色浮法玻璃、鍍膜玻璃、鋼化玻璃、夾層玻璃等.應(yīng)防止運用普通平板玻璃,普通平板玻璃的透明度及強度均達不到要求。上述玻璃原片有必要契合相應(yīng)標準要求,經(jīng)查驗合格后才能運用

The original glass used in the production of hollow glass equipment can be colorless float glass, coated glass, tempered glass, laminated glass, etc. The use of ordinary flat glass should be avoided, as the transparency and strength of ordinary flat glass cannot meet the requirements. The above-mentioned glass raw materials must meet the corresponding standard requirements and can only be used after passing inspection

1、中空玻璃設(shè)備不同廠家不同批次的玻璃在切開前應(yīng)先查看有無色差，將色差較大的玻璃分別用于不同的工程或不同的建筑立面中。玻璃切開尺寸應(yīng)按圖紙要求嚴格執(zhí)行。

1. Before cutting, glass from different manufacturers and batches of insulated glass equipment should be checked for color differences. Glass with larger color differences should be used in different projects or building facades. The cutting size of glass should be strictly executed according to the drawing requirements.

一起操作人員應(yīng)注意玻璃表面，不得有劃傷、氣泡等顯著缺陷。鋁條、插角的選用：鋁條的厚度應(yīng)在0.30mm~0.35mm之間，厚度應(yīng)均勻一致。

Operators should pay attention to the surface of the glass and avoid any significant defects such as scratches or bubbles. Selection of aluminum strips and insertion angles: The thickness of aluminum strips should be between 0.30mm and 0.35mm, and the thickness should be uniform and consistent.

透氣孔散布均勻。鋁條須經(jīng)陽極氧化處理或去污處理，一定要選用質(zhì)量好、層次高的產(chǎn)品，提高鋁條利用率。插角尺寸要選好，表面要擦干凈。

The ventilation holes are evenly distributed. Aluminum bars must undergo anodizing or decontamination treatment, and high-quality and high-level products must be selected to improve the utilization rate of aluminum bars. The size of the insertion angle should be selected well, and the surface should be wiped clean.

中空玻璃設(shè)備

Hollow glass equipment

2、中空玻璃設(shè)備完善中空玻璃出產(chǎn)環(huán)境，中空玻璃在無灰塵、無溶劑污染、溫度適合的環(huán)境中出產(chǎn)，出產(chǎn)車間灰塵污染會對中空玻璃密封體系各個構(gòu)件的粘接效果發(fā)生很大的不利影響。

2. Hollow glass equipment improves the production environment for hollow glass. Hollow glass is produced in an environment free of dust, solvent pollution, and suitable temperature. Dust pollution in the production workshop can have a significant adverse impact on the bonding effect of various components of the hollow glass sealing system.

3、中空玻璃設(shè)備在玻璃材料給定后，比方普通平板玻璃或鋼化玻璃，那么根據(jù)玻璃強度設(shè)計理論，玻璃原片的斷裂強度就確定下來了。由于中空玻璃機器出產(chǎn)的玻璃是由兩片（或兩片以上）玻璃構(gòu)成。

3. After the glass material is given, such as ordinary flat glass or tempered glass, the fracture strength of the original glass sheet is determined based on the glass strength design theory for insulated glass equipment. Due to the fact that the glass produced by the insulated glass machine is composed of two (or more) pieces of glass.

窯爐周邊密封構(gòu)成一個密封的空氣層，中空玻璃在一面玻璃受到載荷作用時，受力面玻璃變形緊縮中空層氣體，氣體壓強增大，將部分載荷傳送給另一面玻璃。

The sealing around the kiln forms a sealed air layer. When one side of the hollow glass is subjected to a load, the glass on the stress surface deforms and compresses the gas in the hollow layer, increasing the gas pressure and transmitting part of the load to the other side of the glass.